Site na mmepe nke ụlọ ọrụ na-emepụta ụgbọ ala, ahịa nke aluminom alloy impact beam na-etokwa ngwa ngwa, n'agbanyeghị na ọ ka dị ntakịrị n'ozuzu ya. Dị ka amụma sitere na Automotive Lightweight Technology Innovation Alliance maka China aluminom alloy impact beam market, ka ọ na-erule 2025, a na-eche na ọchọrọ ahịa dị ihe dị ka tọn 140,000, yana nha ahịa na-atụ anya iru 4.8 ijeri RMB. Ka ọ na-erule 2030, a na-atụ anya na ahịa ahịa ga-adị ihe dị ka tọn 220,000, yana atụmatụ ahịa ahịa ruru ijeri RMB 7.7, yana ọnụ ahịa uto kwa afọ nke ihe dịka 13%. Usoro mmepe nke ịdị arọ na uto ngwa ngwa nke ụdị ụgbọ ala dị n'etiti ruo na njedebe bụ ihe dị mkpa na-anya ụgbọ ala maka mmepe nke aluminom alloy mmetụta ibé na China. Atụmanya ahịa maka igbe mkpọka ọkụ ọkụ ọkụ na-ekwe nkwa.
Ka ọnụ ahịa na-ebelata na teknụzụ na-aga n'ihu, aluminom alloy n'ihu mmetụta ibé na igbe okuku na-eji nwayọọ nwayọọ na-agbasawanye. Ugbu a, a na-eji ha n'ụdị ụgbọ ala etiti ruo elu dị ka Audi A3, Audi A4L, usoro BMW 3, BMW X1, Mercedes-Benz C260, Honda CR-V, Toyota RAV4, Buick Regal, na Buick LaCrosse.
Aluminom alloy mmetụta béam bụ tumadi mejupụtara mmetụta crossbeams, okuku igbe, arịọnụ baseplates, na ịdọrọ nko aka uwe, dị ka e gosiri na Figure 1.
Ọgụgụ 1: Mgbakọ Mgbakọ Mmetụta Aluminom Alloy
Igbe ihe mberede ahụ bụ igbe ígwè dị n'etiti oghere mmetụta na oghere abụọ ogologo oge nke ụgbọ ala ahụ, na-eje ozi dị ka ihe na-ebu ike. Ike a na-ezo aka na ike nke mmetụta. Mgbe ụgbọ ala na-enweta nkukota, mmetụta mmetụta nwere ogo ụfọdụ nke ike na-anata ike. Otú ọ dị, ọ bụrụ na ike ahụ karịrị ike nke mmetụta mmetụta, ọ ga-ebufe ike na igbe okuku. Igbe mkpọka ahụ na-amịkọrọ ike mmetụta niile ma gbanwee onwe ya, na-ahụ na ogwe ogologo ogologo na-adịgide adịgide.
1 Ngwaahịa chọrọ
1.1 Akụkụ ga-agbasorịrị ihe achọrọ ndidi nke eserese, dị ka egosiri na eserese 2.
1.3 chọrọ ịrụ ọrụ igwe:
Ike nkwụsị: ≥215 MPa
Ike Mpụta: ≥205 MPa
Mgbatị A50: ≥10%
1.4 Igbe okuku na-arụ ọrụ:
N'akụkụ X-axis nke ụgbọ ala ahụ, na-eji nkukota elu karịa akụkụ obe nke ngwaahịa ahụ, buru ibu na ọsọ nke 100 mm / min ruo mgbe ọ na-egwepịa ya, yana ọnụọgụ mkpakọ nke 70%. Ogologo mbụ nke profaịlụ bụ 300 mm. Na nkwụsị nke ọgịrịga na-eme ka ọ dị ike na mgbidi dị n'èzí, mgbawa kwesịrị ịbụ ihe na-erughị 15 mm ka e weere na a nabatara ya. Ekwesịrị ijide n'aka na mgbawa a na-ekwe ka ọ ghara imebi ike nke na-akụpịa profaịlụ profaịlụ, ọ dịghịkwa ihe mgbawa dị ịrịba ama na mpaghara ndị ọzọ mgbe ọ nwụsịrị.
2 Ụzọ mmepe
Iji mezuo ihe achọrọ maka ịrụ ọrụ igwe na arụrụ arụ ọrụ, usoro mmepe bụ nke a:
Jiri mkpanaka 6063B nwere ihe mejupụtara alloy bụ isi nke Si 0.38-0.41% na mg 0.53-0.60%.
Mee nkwụsị ikuku na ịka nká iji nweta ọnọdụ T6.
Were alụlụ+ ikuku kwụsị ma mee ọgwụgwọ ịka nká iji nweta ọnọdụ T7.
3 Mmepụta pilot
3.1 Ọnọdụ extrusion
A na-emepụta mmepụta ihe na 2000T extrusion press na extrusion ratio nke 36. Ihe eji eme ihe bụ homogenized aluminum mkpanaka 6063B. The kpo oku okpomọkụ nke aluminum mkpanaka bụ dị ka ndị a: IV mpaghara 450-III mpaghara 470-II mpaghara 490-1 mpaghara 500. Isi cylinder si itunanya mgbali bụ gburugburu 210 mmanya, na anụ extrusion frasi nwere extrusion mgbali nso 180 mmanya. . The extrusion shaft ọsọ bụ 2.5 mm / s, na profaịlụ extrusion ọsọ bụ 5.3 m / min. Okpomọkụ dị na mpụga extrusion bụ 500-540C. A na-eme nkwụsị ahụ site na iji ikuku jụrụ oyi na ike fan aka ekpe na 100%, ike onye ofufe etiti na 100%, yana ikike fan nri na 50%. Nkezi ọnụego jụrụ oyi na mpaghara quenching na-eru 300-350ºC/min, na okpomọkụ mgbe ịpụsịrị mpaghara quenching bụ 60-180ºC. Maka alụlụụ + ikuku quenching, nkezi ọnụego jụrụ oyi n'ime mpaghara kpo oku ruru 430-480 Celsius C / min, na ọnọdụ okpomọkụ mgbe ịpụsịrị mpaghara quenching bụ 50-70 Celsius. Profaịlụ ahụ egosighi ọgbaghara dị mkpa.
3.2 ịka nká
N'ịgbaso usoro ịka nká T6 na 185 ° C maka awa 6, ike nke ihe na ihe eji arụ ọrụ bụ ndị a:
Dị ka usoro ịka nká T7 si dị na 210 ° C maka awa 6 na awa 8, ihe siri ike na ihe eji arụ ọrụ bụ ndị a:
Dabere na data nnwale, alụlụ + ikuku ikuku, jikọtara ya na usoro ịka nká nke 210 Celsius C / 6h, na-emezu ihe achọrọ maka ịrụ ọrụ igwe yana nnwale ngwepịa. N'ịtụle ọnụ ahịa bara uru, a na-ahọrọ alụlụụ + ikuku ikuku na usoro ịka nká 210 ° C / 6h maka mmepụta iji mezuo ihe ngwaahịa ahụ chọrọ.
3.3 Nnwale ịkụpịa
Maka mkpanaka nke abụọ na nke atọ, a na-ebipụ isi isi site na 1.5m, a na-ebipụkwa ọdụ ọdụ site na 1.2m. A na-ewepụta ihe nlele abụọ nke ọ bụla site na ngalaba isi, etiti na ọdụ ọdụ, ogologo ya ruru 300mm. A na-eme ule nchicha mgbe ịka nká na 185 ° C / 6h na 210 ° C / 6h na 8h (data arụmọrụ nke igwe dịka ekwuru n'elu) na igwe nyocha ihe nke ụwa. A na-eme ule ndị a na ọsọ nbudata nke 100 mm / min yana ọnụọgụ mkpakọ nke 70%. Nsonaazụ bụ dị ka ndị a: maka alụlụụ + ikuku quenching na 210 ° C / 6h na 8h usoro ịka nká, ule ndị na-akụpịa ihe na-emezu ihe ndị a chọrọ, dị ka e gosiri na foto 3-2, ebe ihe nlele ikuku na-egosiputa mgbawa maka usoro ịka nká niile. .
Dabere na nsonaazụ ule na-etipịa, alụlụ + ikuku quenching na usoro ịka nká 210 Celsius C/6h na 8h na-emezu ihe ndị ahịa chọrọ.
4 Nkwubi okwu
The njikarịcha nke quenching na ịka nká usoro dị oké mkpa maka na-aga nke ọma mmepe nke ngwaahịa na-enye ezigbo usoro ngwọta maka okuku igbe ngwaahịa.
Site na nnwale sara mbara, e kpebisiri ike na ọnọdụ ihe maka ngwaahịa igbe okuku kwesịrị ịbụ 6063-T7, usoro mmenyụ bụ alụlụụ + ikuku jụrụ oyi, na usoro ịka nká na 210 Celsius C / 6h bụ nhọrọ kacha mma maka iwepu mkpanaka aluminum. na okpomọkụ sitere na 480-500 Celsius C, ngwa ngwa extrusion bụ 2.5 mm / s, extrusion anwụ okpomọkụ nke 480 ° C, na extrusion mpụta okpomọkụ nke 500-540 ° C.
May Jiang deziri site na MAT Aluminum