N'oge ọgwụgwọ okpomọkụ nke aluminom na aluminom alloys, a na-enwekarị nsogbu dị iche iche, dịka:
-Edobe akụkụ na-ezighị ezi: Nke a nwere ike iduga nrụrụ akụkụ, mgbe mgbe n'ihi nkwụsị ọkụ na-ezughị ezu site na nkwụsị nke na-eme ka ọ bụrụ ngwa ngwa ngwa ngwa iji nweta ihe ndị a chọrọ.
- kpo oku ngwa ngwa: Nke a nwere ike ime ka nrụrụ ọkụ; akụkụ kwesịrị ekwesị na-enyere aka hụ na ọbụna kpo oku.
-Ikpo oke ọkụ: Nke a nwere ike ibute agbaze akụkụ ma ọ bụ agbaze eutectic.
-Mkpa n'elu / elu-okpomọkụ oxidation.
-Ngwọta ịka nká karịrị oke ma ọ bụ ezughi oke, nke abụọ nwere ike ịkpata ihe ndị na-emepụta ihe.
-Mgbanwe na oge / okpomọkụ / quenching parameters nwere ike ime ka deviations na n'ibu na / ma ọ bụ anụ ahụ Njirimara n'etiti akụkụ na batches.
-Na mgbakwunye, otu ọnọdụ okpomọkụ adịghị mma, oge mkpuchi ezughị ezu, na oyi na-adịghị mma n'oge ọgwụgwọ okpomọkụ ngwọta nwere ike inye aka na-adịghị mma.
Ọgwụgwọ okpomọkụ bụ usoro ikpo ọkụ dị oke mkpa na ụlọ ọrụ aluminom, ka anyị banye n'ime ihe ọmụma metụtara ya.
1.Pre-ọgwụgwọ
Usoro ọgwụgwọ tupu emee nke na-eme ka nhazi ahụ dịkwuo mma ma na-ebelata nchekasị tupu ịkwụsị ya bara uru maka ibelata mgbagwoju anya. Ọgwụgwọ tupu ọgwụgwọ na-agụnye usoro dị ka spheroidizing annealing na mgbakasị ahụ mgbakasị ahụ, ụfọdụ na-ewerekwa quenching na tempering ma ọ bụ normalize ọgwụgwọ.
Ịkwụsị Enyemaka Nchegbu: N'oge ị na-arụ ọrụ, nrụgide ndị fọdụrụ nwere ike ịmalite n'ihi ihe ndị dị ka usoro nhazi, ntinye ngwá ọrụ, na ịcha ọsọ. Nkesa na-ezighi ezi nke nrụgide ndị a nwere ike ibute mgbagha mgbe ị na-emenyụ. Iji belata mmetụta ndị a, ọ dị mkpa ka a na-ewepụ ihe mgbakasị ahụ tupu emenyụọ. Okpomọkụ maka mgbakasị ahụ mgbu na-abụkarị 500-700 Celsius. Mgbe a na-ekpo ọkụ na ikuku ikuku, a na-eji okpomọkụ nke 500-550 ° C na-ejide oge nke awa 2-3 iji gbochie oxidation na decarburization. Ekwesịrị ịtụle mgbagha akụkụ n'ihi ịdị arọ nke onwe ya n'oge nbudata, na usoro ndị ọzọ yiri nke annealing ọkọlọtọ.
Ọgwụ Preheat maka Mmelite Ọdịdị: Nke a na-agụnye spheroidizing annealing, quenching na tempering, normalize ọgwụgwọ.
-Spheroidizing Annealing: Dị mkpa maka carbon ngwá ọrụ ígwè na alloy ngwá ọrụ ígwè n'oge okpomọkụ ọgwụgwọ, Ọdịdị nwetara mgbe spheroidizing annealing budata emetụta distortion na-emekarị n'oge quenching. Site n'ịgbanwe usoro nhazi nke post-annealing, mmadụ nwere ike ibelata mgbagha mgbe niile n'oge nkwụsị.
-Ụzọ ọgwụgwọ ndị ọzọ: Enwere ike iji ụzọ dị iche iche iji belata mgbagha na-emenyụ ọkụ, dị ka imenyụ na iwe ọkụ, na-eme ka ọgwụgwọ dị mma. Ịhọrọ usoro ọgwụgwọ kwesịrị ekwesị dị ka quenching na tempering, normalizing ọgwụgwọ dabere na ihe kpatara mgbagha na ihe nke akụkụ ahụ nwere ike ibelata mgbagwoju anya. Otú ọ dị, ịkpachara anya dị mkpa maka nrụgide fọdụrụnụ na ike siri ike na-abawanye mgbe iwe ọkụ gasịrị, karịsịa ọgwụgwọ na-ekpo ọkụ na nke na-ekpo ọkụ nwere ike ibelata mgbasawanye n'oge nkwụsị maka ígwè nwere W na Mn, ma ọ nwere mmetụta dị nta na ibelata nrụrụ maka ígwè dị ka GCr15.
N'ime mmepụta ihe bara uru, ịchọpụta ihe na-eme ka ọ kwụsị ịgbagha, ma ọ bụ n'ihi nrụgide fọdụrụnụ ma ọ bụ usoro adịghị mma, dị mkpa maka ọgwụgwọ dị irè. Ekwesịrị ịme mgbatị ahụ mgbakasị ahụ maka mgbagha nke nrụgide ndị fọdụrụnụ kpatara, ebe ọgwụgwọ dị ka iwe ọkụ nke na-agbanwe usoro ahụ adịghị mkpa, yana ọzọ. Naanị mgbe ahụ ka enwere ike imezu ebumnuche nke ibelata mgbaghara iji belata ọnụ ahịa ma hụ na ịdị mma.
2.Quenching Heating Ọrụ
Okpomọkụ na-emenyụ: The quenching okpomọkụ na-emetụta nnọọ agbagọ. Anyị nwere ike nweta ebumnuche nke ibelata nrụrụ site n'ịgbanwe ọnọdụ okpomọkụ na-ekpo ọkụ, ma ọ bụ ihe nkwụnye ego echekwara bụ otu ihe ahụ dị ka okpomọkụ na-ekpo ọkụ iji nweta nzube nke mbenata nrụrụ, ma ọ bụ nke ezi uche dị na ya ahọpụtara ma debe ya machining allowance na quenching okpomọkụ mgbe ule ọgwụgwọ okpomọkụ gasịrị. , ka ibelata ụgwọ ọrụ machining na-esote. Mmetụta nke quenching okpomọkụ na quenching deformation abụghị nanị metụtara ihe eji eme ihe na workpiece, kamakwa metụtara nha na ọdịdị nke workpiece. Mgbe udi na size nke workpiece dị nnọọ iche, ọ bụ ezie na ihe nke workpiece bụ otu ihe ahụ, quenching deformation omume bụ nnọọ iche, na onye ọrụ kwesịrị ntị na ọnọdụ a na n'ezie mmepụta.
Oge Njide Quenching: Nhọrọ nke ijide oge ọ bụghị naanị na-eme ka ikpo ọkụ zuru oke ma nweta ike siri ike ma ọ bụ ihe eji arụ ọrụ mgbe emenyụchara ma na-atụlekwa mmetụta ya na mgbagwoju anya. Ịgbatị oge nkwụsịtụ na-abawanye okpomọkụ na-ekpochapụ, karịsịa nke a na-akpọ maka carbon dị elu na ígwè chromium dị elu.
Ụzọ ntinye: Ọ bụrụ na workpiece etinye na ihe ezi uche na-adịghị n'ụdị n'oge kpo oku, ọ ga-eme ka deformation n'ihi na arọ nke workpiece ma ọ bụ deformation n'ihi na ibe extrusion n'etiti workpieces, ma ọ bụ deformation n'ihi na-erughị eru kpo oku na jụrụ n'ihi oke stacking nke workpieces.
Usoro kpo oku: N'ihi na mgbagwoju-ekara na iche iche ọkpụrụkpụ workpieces, karịsịa ndị nwere elu carbon na alloy ọcha, a ngwa ngwa na edo kpo oku usoro dị oké mkpa. Iji preheating na-adịkarị mkpa, mgbe ụfọdụ na-achọ ọtụtụ okirikiri ọkụ ọkụ. N'ihi na ibu workpieces adịghị irè mesoo site preheating, iji igbe na-eguzogide ọkụ na-achịkwa kpo oku nwere ike ibelata distortion mere site ngwa ngwa kpo oku.
3. Ọrụ jụrụ oyi
Nrụrụ emenyụ na-esite na usoro jụrụ oyi. Nhọrọ ndị na-emenyụ ọkụ kwesịrị ekwesị, ịrụ ọrụ nke ọma, na nzọụkwụ ọ bụla nke usoro jụrụ oyi na-emetụta kpọmkwem nrụrụ.
Nhọrọ Ọkara na-emenyụ: Ka ị na-ahụ na ike siri ike a chọrọ ka emechie ya, a ga-ahọrọ usoro mgbasa ozi na-emenyụ obere obere iji belata mgbagha. Iji ihe ndị na-ekpo ọkụ na-ekpo ọkụ maka ịsa ahụ dị jụụ (iji mee ka ọ dị mfe ịgbatị mgbe akụkụ ahụ ka na-ekpo ọkụ) ma ọ bụ ọbụna oyi na-atụ aro. Ọkara nwere ọnụego jụrụ oyi n'etiti mmiri na mmanụ nwekwara ike dochie igwe mmiri-mmanụ abụọ.
-Ikuku jụrụ oyi: Ikuku ikuku na-ekpo ọkụ na-arụ ọrụ dị irè maka ibelata nrụrụ nke nkwụsị nke ígwè dị elu, ígwè chromium na-eme ka ọkpụkpụ na-eme ka ikuku dị jụụ micro-deformation ígwè. Maka ígwè 3Cr2W8V nke na-adịghị achọ ike siri ike mgbe emenyụchara, ikuku quenching nwekwara ike iji belata nrụrụ site n'ịgbanwee nke ọma okpomọkụ.
- Mmanụ jụrụ oyi na imenyụ: mmanụ bụ a quenching ọkara na a ukwuu ala jụrụ ọnụego karịa mmiri, ma n'ihi na ndị workpieces na elu hardenability, obere size, mgbagwoju udi na nnukwu deformation ọchịchọ, jụrụ ọnụego mmanụ dị oke elu, ma maka workpieces na obere size ma ogbenye. hardenability, jụrụ ọnụego mmanụ bụ ezughi oke. Iji dozie esemokwu ndị a dị n'elu ma na-eji mmanụ ọkụ eme ihe n'ụzọ zuru ezu iji belata deformation nke workpieces, ndị mmadụ nakweere ụzọ nke imezi okpomọkụ mmanụ na ịba ụba quenching okpomọkụ iji gbasaa ojiji nke mmanụ.
- Ịgbanwe okpomọkụ nke mmanụ ọkụ: iji otu okpomọkụ mmanụ maka quenching iji belata quenching deformation ka nwere nsogbu ndị a, ya bụ, mgbe mmanụ ọkụ dị ala, nrụrụ na-emenyụ ka dị ukwuu, na mgbe mmanụ ọkụ dị elu, ọ na-esiri ike ịhụ na workpiece mgbe quenching ike. N'okpuru ngwakọta nke udi na ihe onwunwe nke ụfọdụ workpieces, ịba ụba okpomọkụ nke mmanụ quenching nwekwara ike ịbawanye nrụrụ ya. Ya mere, ọ dị ezigbo mkpa iji chọpụta okpomọkụ mmanụ nke mmanụ na-emenyụ ọkụ mgbe ọ gafesịrị ule ahụ dị ka ọnọdụ n'ezie nke ihe eji arụ ọrụ, akụkụ nke akụkụ na ọdịdị.
Mgbe ị na-eji mmanụ ọkụ na-ekpo ọkụ na-emenyụ ọkụ, iji zere ọkụ na-akpata site na nnukwu mmanụ ọkụ na-eme ka ọ dị ọkụ na-eme ka ọ dị jụụ, a ghaghị ịkwado ngwá ọrụ ọkụ ọkụ dị mkpa n'akụkụ tank mmanụ. Tụkwasị na nke ahụ, e kwesịrị ịnwale ndenye mmanye nke mmanụ na-emenyụ ọkụ mgbe niile, a ga-agbanyekwa mmanụ ọhụrụ ma ọ bụ dochie ya n'oge.
-Mbawanye okpomọkụ na-emenyụ ọkụ: Nke a na usoro adabara obere cross-ngalaba carbon ígwè workpieces na ubé ibu alloy ígwè workpieces na-apụghị izute ekweghị ekwe chọrọ mgbe kpo oku na okpomọkụ ichekwa na nkịtị quenching okpomọkụ na mmanụ quenching. Site n'ịbawanye okpomọkụ na-ekpo ọkụ n'ụzọ kwesịrị ekwesị wee kwụsị mmanụ, enwere ike nweta mmetụta nke ike siri ike na ibelata nrụrụ. Mgbe ị na-eji usoro a emenyụ, ekwesịrị ịkpachara anya iji gbochie nsogbu ndị dị ka ịkwanye ọka, mbelata akụrụngwa akụrụngwa na ndụ ọrụ nke workpiece n'ihi ụbara quenching okpomọkụ.
- klaasị na austempering: Mgbe quenching hardness nwere ike izute imewe chọrọ, na nkewa na austempering nke na-ekpo ọkụ na-ajụ na-ajụ kwesịrị n'ụzọ zuru ezu tinye n'ọrụ iji nweta nzube nke mbenata quenching deformation. Usoro a dịkwa irè maka obere ike, obere akụkụ carbon structural ígwè na ígwè ngwá ọrụ, karịsịa chromium-nwere anwụ ígwè na elu-ọsọ ígwè workpieces na elu hardenability. Nkewa nke usoro ịsa ahụ na-ekpo ọkụ na usoro jụrụ oyi nke austempering bụ ụzọ nkwụsị nke isi maka ụdị ígwè a. N'otu aka ahụ, ọ dịkwa irè maka ndị carbon steels na ala-alloy structural steels na-adịghị achọ nnukwu quenching ike.
Mgbe ị na-emenyụ ọkụ na-ekpo ọkụ, a ga-aṅa ntị na okwu ndị a:
Nke mbụ, mgbe a na-eji mmanụ bat maka grading na isothermal quenching, mmanụ ọkụ kwesịrị ịchịkwa nke ọma iji gbochie ọkụ ọkụ.
Nke abụọ, mgbe ị na-emenyụ ya na ọkwa nnu nitrate, tankị nnu nitrate kwesịrị inwe ngwá ọrụ dị mkpa na ngwaọrụ mmiri jụrụ oyi. Maka ịkpachara anya ndị ọzọ, biko rụtụ aka na ozi dị mkpa, ma agaghị emeghachi ha ebe a.
Nke atọ, a ghaghị ịchịkwa okpomọkụ nke isothermal n'oge nkwụsị nke isothermal. Okpomọkụ dị elu ma ọ bụ dị ala adịghị akwado ibelata nrụrụ. Na mgbakwunye, n'oge austempering, a ga-ahọrọ usoro nghọta nke workpiece iji gbochie nrụrụ nke ịdị arọ nke workpiece kpatara.
Nke anọ, mgbe ị na-eji isothermal ma ọ bụ graded quenching iji mezie ọdịdị nke workpiece mgbe ọ na-ekpo ọkụ, ngwá ọrụ na ihe ndozi kwesịrị ịkwado nke ọma, ihe omume kwesịrị ịdị ngwa ngwa n'oge ọrụ. Gbochie mmetụta ọjọọ na quenching àgwà nke workpiece.
Ọrụ jụrụ oyi: Ịrụ ọrụ nkà n'oge usoro jụrụ oyi na-enwe mmetụta dị ukwuu na nrụrụ emenyụ, karịsịa mgbe a na-eji mmiri ma ọ bụ mmanụ na-emenyụ ihe.
-Ntụziaka ziri ezi nke ntinye Ọkara Quenching: A, symmetrically itule ma ọ bụ elongated mkpara-dị ka workpieces kwesịrị ekwesị quenched n'ime ọkara. Enwere ike imenyụ akụkụ asymmetric n'otu akụkụ. Ntụziaka ziri ezi bụ iji hụ na oyi na-atụ n'otu n'akụkụ niile, yana ebe ndị na-ajụ oyi na-eji nwayọọ na-abanye na ọkara nke mbụ, na-esote ngalaba jụrụ oyi ngwa ngwa. Ịtụle ọdịdị nke workpiece na mmetụta ya na ọsọ jụrụ oyi dị mkpa na omume.
-Movement nke Workpieces na Quenching Ọkara: Akụkụ ndị na-eme ka ahụ dị nwayọọ kwesịrị iche ihu na-emenyụ ọkụ. Workpieces nwere ụdị Symmetric kwesịrị ịgbaso ụzọ ziri ezi na nke edo na ọkara, na-ejigide obere njupụta na mmegharị ngwa ngwa. Maka ihe ndị dị mkpa na elongated workpieces, nkwụsi ike n'oge quenching dị oké mkpa. Zere ịkwagharị ma tụlee iji clamps kama ijikọ waya maka njikwa ka mma.
-Ọsọ nke Quenching: Ekwesịrị imenyụ ihe arụ ọrụ ngwa ngwa. Karịsịa maka mkpara dị ka mkpara workpieces, iji nwayọọ na-emenyụ ọsọ nwere ike iduga nrụrụ na-agbagọ agbagọ na ndịiche na nrụrụ n'etiti ngalaba kwụsịrị n'oge dị iche iche.
-Achịkwaa jụrụ oyi: N'ihi na workpieces na ịrịba iche na cross-ngalaba size, chebe ngwa ngwa-ajụjụ ọnụ ngalaba na ihe dị ka asbestos eriri ma ọ bụ metal Ibé akwụkwọ iji belata ha jụrụ ọnụego na nweta edo jụrụ.
-Oge oyi na mmiri: N'ihi na workpieces tumadi na-enwe deformation n'ihi structural nchegbu, ebelata ha jụrụ oge na mmiri. N'ihi na workpieces bụ isi na-enwe nrụrụ n'ihi thermal nrụgide, ịgbatị ha jụrụ oyi na mmiri iji belata quenching deformation.
May Jiang deziri site na MAT Aluminum